Organic white light emitting devices with an RGB stacked multilayer structure

White organic light emitting devices (OLEDs) with an RGB stacked multilayer structure are demonstrated. In RGB staked OLEDs, blue emitting 1,4-bis[2, 2-diphenylvinyl]biphenyl (DPVBi), green emitting quinacridane (QD), and red emitting [2,6-bis[2-[5-(dibutylamino)phenyl]vinyl]-4H-pyran-4-ylidene]propanedinitrile (DADB) were used. Through the optimization of the device structure, the pure white light emission with CIE coordinates of (0.33,0.33) at 20 mA/cm ² was obtained, at which the color temperature and color rendering index were 5560 K and 79, respectively. Its maximum luminance was 14,000 cd/m² at 12.6 V, and the luminance efficiency was 1.34 lm/W at 100 cd/m².